产品规格书/Specification
|
产品/product: |
氧化铝陶瓷发热电阻浆料/ Alumina ceramic board heating Resist paste |
|
料号/Part number: |
05H18 |
适用范围/Application:
此产品适用于氧化铝陶瓷加热电路使用。
The resist paste applies to alumina ceramic heating resistor paste.
使用条件/Operating conditions：
|
基材 Substrate |
氧化铝陶瓷 Alumina ceramic |
|
印刷 Printing |
200-250目丝网印刷 200-250 mesh stainless screen |
|
流平 Levelling |
室温下流平5-15分钟（时间根据流平的实际情况决定）。 5-15min minutes at room temperature |
|
干燥 Drying |
通风烘箱烘烤100-150℃，10-15分钟 （烘考温度低于300℃，可根据烘烤的实际情况决定烘烤时间。） 100-150℃ 10-15 min |
|
烧结 Firing Condition |
隧道炉空气气氛下烧结，峰值850℃（推荐值），10分钟。 Atmospheric firing in belt furnace with peak time of 10 Minutes at 850℃ |
|
Thinner |
ST1001 |
性能/Characteristics：
1. 浆料性能/Paste Characteristics：
|
性能Characteristic |
标准Standard |
测试方法及条件 Test method and conditions |
|
|
1 |
Fineness |
≤8μm |
FOG test |
|
2 |
Viscosity |
120-280Pa.s |
Brookfield HBT utility cup and spindle (SC4-14/6R), 10rpm, 25±1℃， Brookfield HBT（博利飞）粘度计， 转子SC4-14/6R), 10rpm, 25±1℃ 粘度可根据用户实际需要调节。 |
2. 烧结后特性/Characteristics after firing：
在1烧结条件下，膜厚8-12mm Check fired film produced under the conditions specified in 1）, (Film thickness is 8-12mm.)
|
特性 Characteristics |
Standard 标准 |
测试方法和条件 Test method and conditions |
|
|
3 |
外观 Appearance |
紧凑，致密 Compact and unknit |
Eyeballing |
|
4 |
方阻值 Resistivity |
如下表格 As below form |
标准膜厚10μm Standard film thickness is 10mm. |
|
温度系数 TCR |
如下表格 As below form |
HTCR 25-125℃ |
|
|
产品系列 |
氧化铝陶瓷发热电阻浆料 Alumina ceramic board heating Resist paste |
|||
|
P/N |
resistivity (Ω/□) |
TCR (ppm/℃) |
烧结温度℃ Sintering |
viscosity (kcps) |
|
05H18-0R005xx |
0.01 |
后两位xx代表温度系数,例如 The last two letters repreent TCR (ppm/℃)
30--->3000ppm 15--->1500ppm 12--->1200ppm 05--->500ppm 03--->300ppm
|
850℃ |
120～280 |
|
05H18-0R010xx |
0.01 |
|||
|
05H18-0R020xx |
0.02 |
|||
|
05H18-0R030xx |
0.03 |
|||
|
05H18-0R050xx |
0.05 |
|||
|
05H18-0R100xx |
0.10 |
|||
|
05H18-0R200xx |
0.20 |
|||
|
05H18-0R300xx |
0.30 |
|||
|
05H18-0R500xx |
0.50 |
|||
|
05H18-1R000xx |
1.00 |
|||
|
05H18-3R000xx |
3.00 |
|||
|
05H18-4R000xx |
4.00 |
|||
|
05H18-5R000xx |
5.00 |
|||
|
05H18-011xx |
10.00 |
|||
|
05H18-021xx |
20.00 |
|||
|
05H18-051xx |
50.00 |
|||
|
05H18-101xx |
||||